عرض بسيط للتسجيلة

المؤلفWang T.
المؤلفQiblawey H.
المؤلفJudd S.
المؤلفBenamor A.
المؤلفNasser M.S.
المؤلفMohammadian A.
تاريخ الإتاحة2019-10-17T07:44:38Z
تاريخ النشر2018
اسم المنشورJournal of Membrane Science
الرقم المعياري الدولي للكتاب3767388
معرّف المصادر الموحدhttp://dx.doi.org/10.1016/j.memsci.2018.02.009
معرّف المصادر الموحدhttp://hdl.handle.net/10576/12155
الملخصThe use of bio-inspired polydopamine (PDA) chemistry for membrane development has attracted increasing interest in recent years. This paper reports on the fabrication of new nanofiltration (NF) membrane with a robust and permeable barrier layer based on dopamine assisted co-deposition strategy. Hydrophilic and hydroxyl-rich polymer poly(vinyl alcohol) (PVA) was used as the key building block for co-deposition, successfully entrapping it within the self-polymerized polydopamine (PDA) matrix with stabilization through intermolecular hydrogen bonding between PVA and PDA moieties. As a result, visibly denser, thicker and more hydrophilic co-deposited layers were formed on polysulfone (PSf) substrates compared to the pure PDA layer. The surface properties of the co-deposited layers were found to be sensitive to the amount of PVA incorporated within the coating layers, while the latter positively correlated with the content of PVA in dopamine coating solution. Further crosslinking with highly electrophilic trimesoyl chloride (TMC) as a covalent linker effectively tightened the co-deposited layers, yielding NF characteristics for the crosslinked membranes with negatively charged features. The NF membranes had notably higher water permeabilities with comparable Na2SO4 rejections at low operation pressures of 2 bar when compared with commercial and several lab-fabricated NF membranes. Furthermore, the NF membrane based on high PVA content of 10 mg mL?1 showed good protein fouling resistance and long-term performance stability. - 2018 Elsevier B.V.
راعي المشروعThis work is supported by grant from the Qatar National Research Fund (QNRF) under its National Priorities Research Program (NPRP) award number NPRP 8�1115-2�473 . The statements made herein are solely the responsibility of the authors. We acknowledge Center of Advanced Materials (CAM, Qatar University) for AFM measurements. Appendix A
اللغةen
الناشرElsevier B.V.
الموضوعCo-deposition
الموضوعCrosslinking
الموضوعNanofiltration membrane
الموضوعPoly(vinyl alcohol)
الموضوعPolydopamine
العنوانFabrication of high flux nanofiltration membrane via hydrogen bonding based co-deposition of polydopamine with poly(vinyl alcohol)
النوعArticle
الصفحات222-233
رقم المجلد552