AuthorAlnahhal, Wael
AuthorTaha, Ramzi
AuthorAl-Nasseri, Hammad
AuthorNishad, Safna
Available date2017-10-17T06:30:11Z
Publication Date2017-08-31
Publication NameKSCE Journal of Civil Engineering
Identifierhttp://dx.doi.org/10.1007/s12205-017-0010-6
CitationAlnahhal, W., Taha, R., Al-Nasseri, H. et al. "Effect of using Cement Kiln Dust as a nano-material on the strength of cement mortars" KSCE Journal of Civil Engineering (2017).
ISSN1226-7988
URIhttp://hdl.handle.net/10576/5696
AbstractIn this experimental study, the effects of using nano-sized Cement Kiln Dust (CKD) as a partial replacement for Ordinary Portland Cement (OPC) on the strength of cement mortars is investigated. The CKD was milled up to 4 hours in a planetary ball mill. In addition to the control cement mortar mixture with 0% CKD, a total of 28 concrete mortar mixtures were prepared with four different replacement percentages of nano-CKD (5, 10, 15, and 20 %), and seven different milling times (1, 1.5, 2, 2.5, 3, 3.5, and 4 hours). The compressive strengths of all cement mortar mixtures were evaluated after curing periods of 7, 28, and 56 days. In addition, the chemical, physical and microscopical properties of the nano-CKD were evaluated using Scanning Electron Microscope (SEM), Transmission Electron Microscope (TEM) and X-ray diffraction (XRD). The experimental results showed that the partial replacement of the OPC with the nano-CKD enhanced the compressive strength of the cement mortar by about 15-30% compared with normal mortar without CKD. Moreover, the experimental results indicated that no change was observed in the chemical composition of CKD after 4 hours of milling. However, there was a decrease in the Portlandite content in parallel with an increase in the density and the surface area.
Languageen
PublisherSpringer Verlag
Subjectball milling
cement kiln dust
cement mortar
compressive strength
nano-material
scanning electron microscopy
TitleEffect of using Cement Kiln Dust as a nano-material on the strength of cement mortars
TypeArticle
Pagination1-8
ESSN1976-3808


Files in this item

FilesSizeFormatView

There are no files associated with this item.

This item appears in the following Collection(s)

Show simple item record